EAA 1430产品说明
EAA 1430技术参数：维卡软化温度： 76.1 °C
溶融温度（DSC）： 96.1 °C
熔流率 2： (190°C/2.16 kg) 5.0 g/10 min
熔体温度：384°F (196°C)
EAA 1430物性数据：
|
产品说明 |
||||||
|
PRIMACOR™ 1430 is an ethylene acrylic acid copolymer that provides good sealability, hot tack and excellent adhesion to polar (foil, nylon, etc.) materials. It also provides excellent toughness, clarity and tear resistance. · Adhesive layer of sealant layer in flexible packaging structures · For blown or cast film extrusion · Used where adhesion to nylon or foil is desired
· U.S. FDA 21 CFR 177.1310(b) · EU, No 10/2011 Consult the regulations for complete details. |
||||||
|
总体 |
|
|||||
|
材料状态 |
· 已商用：当前有效 |
|||||
|
供货地区 |
|
|||||
|
机构评级 |
|
|||||
|
形式 |
· 颗粒料 |
|||||
|
加工方法 |
|
|||||
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|||
|
比重 |
0.930 |
g/cm³ |
ASTM D792, ISO 1183 |
|||
|
熔流率 2 (190°C/2.16 kg) |
5.0 |
g/10 min |
ASTM D1238, ISO 1133 |
|||
|
共聚单体含量 3 |
9.7 |
% |
Internal Method |
|||
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
|
抗张强度 |
|
|
|
|
|
屈服, 模压成型 4 |
7.67 |
MPa |
ASTM D638 |
|
|
屈服, 模压成型 |
7.67 |
MPa |
ISO 527-2/508 |
|
|
断裂, 模压成型 4 |
19.5 |
MPa |
ASTM D638 |
|
|
断裂, 模压成型 |
19.5 |
MPa |
ISO 527-2/508 |
|
|
伸长率 |
|
|
|
|
|
断裂, 模压成型 4 |
580 |
% |
ASTM D638 |
|
|
断裂, 模压成型 |
580 |
% |
ISO 527-2/508 |
|
|
薄膜 |
额定值 |
单位制 |
测试方法 |
|
|
抗张强度 |
|
|
|
|
|
MD: 屈服, 51 µm |
10.4 |
MPa |
ASTM D882 |
|
|
TD: 屈服, 51 µm |
10.2 |
MPa |
ASTM D882 |
|
|
MD: 屈服, 51 µm |
10.4 |
MPa |
ISO 527-3 |
|
|
TD: 屈服, 51 µm |
10.2 |
MPa |
ISO 527-3 |
|
|
MD: 断裂, 51 µm |
30.6 |
MPa |
ASTM D882, ISO 527-3 |
|
|
TD: 断裂, 51 µm |
31.0 |
MPa |
ASTM D882, ISO 527-3 |
|
|
伸长率 |
|
|
ASTM D882, ISO 527-3 |
|
|
MD: 断裂, 51 µm |
420 |
% |
|
|
|
TD: 断裂, 51 µm |
470 |
% |
|
|
|
埃尔曼多夫抗撕强度 5 |
|
|
|
|
|
MD: 51 µm |
470 |
g |
ASTM D1922 |
|
|
TD: 51 µm |
730 |
g |
ASTM D1922 |
|
|
MD: 51 µm |
2100 |
N |
ISO 6383-2 |
|
|
TD: 51 µm |
3300 |
N |
ISO 6383-2 |
|
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
|
维卡软化温度 |
76.1 |
°C |
ASTM D1525, ISO 306 |
|
|
溶融温度（DSC） |
96.1 |
°C |
Internal Method |
|
|
光学性能 |
额定值 |
单位制 |
测试方法 |
|
光泽度 (45°, 50.8 µm) |
74 |
|
ASTM D2457 |
|
雾度 |
|
|
|
|
50.8 µm |
4.0 |
% |
ISO 14782 |
|
50.8 µm |
4.0 |
% |
ASTM D1003 |
|
挤压说明 |
|||
|
挤出涂层薄膜的制造条件： · 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D · 螺杆类型：带 Maddock Mixer 的单跨型 · 模具间隙：40 密尔 (1.0 mm) · 熔体温度：384°F (196°C) · 输出：模具周长的 6 磅/小时/英寸 · 模具直径：6 英寸 · 放大比：2.5:1 · 冷冻线高度：29 英寸 (737 mm) |
|||
EAA 应用领域：
1、粉末涂层：本产品可以制作成粉末可以喷涂于管材（如图三）、钢材、无纺布服装等材料表面，作为防腐或者粘合材料；
2、热熔胶：用于难粘接材料；也可以用于高档服装的衣领中间粘合层；
3、水性溶剂：在适当的反应条件下能溶解于热的碱性溶液，可以配制水性粘合剂，用于服装衣料等；
4、降解环保材料：EAA与淀粉基材料共混可以生产降解塑料。